The influence of crystal-structure imperfections on superconductivity

Abstract

The thesis focuses on investigation of charge-density wave (CDW) and superconduc- tivity (SC) and their relationship to the structure of material. Materials of study are intermetallics with the chemical formula REPt2Si2, where RE = La, Nd, Pr. The lan- thanum sample shows both SC and CDW, while Nd and Pr samples show CDW and specific heat anomaly of magnetic origin. Samples were checked using powder X-ray diffraction and energy-dispersive X-ray spectroscopy. SC, CDW and magnetic transi- tions were observed at temperatures down to 0.4 K with AC resistivity and specific heat measurements. Some properties were compared to already measured data on single crys- tals. Structure of materials was found to impact CDW and SC parameters.

Tato práce se zaměřuje na zkoumání vlny nábojové hustoty (CDW) a supravodivosti (SC) a jejich vztahu ke struktuře materiálu. Studovanými materiály jsou intermetalické sloučeniny s chemickým vzorcem REPt2Si2, kde RE = La, Nd, Pr. Sloučenina s RE = La vykazuje jak SC, tak CDW, zatímco vzorky s RE = Nd a Pr vykazují CDW a anomálii v měrné tepelné kapacitě magnetického původu. Vzorky byly zkoumány pomocí práškové rentgenové difrakce a energiově disperzní rentgenové spektroskopie. CDW a magnetické a SC přechody byly pozorovány při teplotách až k 0,4 K pomocí měření měrné tepelné kapacity a odporu střídavou metodou. Některé vlastnosti byly porovnány s již změřenými výsledky na monokrystalech. Bylo zjištěno, že struktura materiálů ovlivňuje parametry CDW a SC.