Nízkoenergetické zpracování grafitu pomocí elektrickým polem asistovaných technik

Abstract

This thesis focused on testing the validity and effectiveness of high-pressure graphite com- paction. Furthermore, the graphite compaction process was extended to include the application of an electric field, using either a direct current or alternating current. The samples were cha- racterized using X-ray powder diffraction and Raman spectroscopy. Changes in the surface were observed under an optical microscope, and fracture surface was observed using a scanning electron microscope. The microstructure of the tablets - both those unaffected by the electric field and those affected - clearly differed under the optical microscope. Raman spectroscopy indicated an increase in the intensity of the defect band in the graphite lattice, suggesting a certain effect on the resulting compacts. X-ray powder diffraction revealed observable changes in the diffraction patterns of the powder and tablets, as well as between the tablets themselves. Keywords: graphite, compaction, pressing, sintering, electric field

Tato práce se věnovala testování validity a efektivity vysokotlakého lisování grafitu. Dále pak bylo lisování grafitu rozšířeno o aplikaci elektrického pole s aplikací stejnosměrného, nebo stří- davého pole. Vzorky byly charakterizovány práškovou rentgenovou difrakcí, Ramanovou spek- troskopií. Sledovány byly změny povrchu na optickém mikroskopu, či lom na skenovacím elektro- novém mikroskopu. Mikrostruktura proudem neovlivněných a ovlivněných tablet se na optickém mikroskopu jednoznačně liší. Ramanova spektroskopie poukázala na zvýšení intenzity pásu de- fektů v mříži grafitu a tedy určitý efekt na vzniklé kompakty. Prášková rentgenová difrakce poukázala na pozorovatelné změny difraktogramů prášku a tablet, či tablet samotných mezi sebou. Klíčová slova: grafit, kompaktizace, lisování, slinování, electrické pole