Abstract

This thesis deals with crystal structure and magnetic properties of RCr2Si2 (R = Pr, Tb, Er) and RCr2Si2C (R = La, Ce, Pr, Nd) compounds. All prepared samples were characterized by powder X-ray diraction and investigated by specic-heat, magnetization and AC-susceptibility measurements in the temperature range 2-900 K and in magnetic elds up to 9 T. The results suggest non-trivial magnetic ordering of the Cr sublattice in all studied compounds, accompanied with ferromagnetic ordering of the Pr and Nd magnetic moments below the Curie temperature of 30 and 21 K in PrCr2Si2C and NdCr2Si2C, respectively, and possible metamagnetism in CeCr2Si2C. For RCr2Si2C compounds, the experimental evidence of Cr magnetism is corroborated by results of extended rst-principles calculations based on the density functional theory.

Tato práce studuje krystalovou strukturu a magnetické vlastnosti sloučenin typu RCr2Si2 (R = Pr, Tb, Er) a RCr2Si2C (R = La, Ce, Pr, Nd). Všechny připravené vzorky byly charakterizovány pomocí praškové rentgenové difrakce a zkoumány pomocí měření tepelné kapacity, magnetizace a střídavé susceptibility v teplotním rozsahu 2-900 K a v magnetických polích do 9 T. U všech studovaných sloučenin výsledky ukazují na netriviální magnetické uspořádání chromové podmřížky. Dále bylo pozorováno feromagnetické uspořádání vzácnozeminné podmřížky ve sloučeninách PrCr2Si2C a NdCr2Si2C, a také metamagnetismus v CeCr2Si2C. Pro sloučeniny RCr2Si2C jsme vypočítali hustotu stavů z prvních principů pomocí teorie funkcionálu hustoty. Tyto výpočty potvrzují přítomnost magnetického momentu chromu v těchto sloučeninách.