Abstract

In the presented thesis, metal-organic framework (MOF) PCN-222 was post-synthetically modified with diphenylphosphinic acid. The parent PCN-222 and modified MOFs were characterized by powder X-ray diffractions and nitrogen adsorption isotherms. The presence of bound diphenylphosphinic acid in the modified MOFs was documented by inductively coupled plasma optical emission spectrometry, infrared spectroscopy, and 13 C and 31 P solid- state NMR. The modified MOFs have greater water-drying stability and up to four times higher singlet oxygen productivity under visible light irradiation than the parent PCN-222. Keywords: metal-organic framework, porphyrin, post-synthetic modifications, diphenylphosphinic acid, singlet oxygen, stability

V předkládané bakalářské práci byla organokovová síť (MOF) PCN-222 postsynteticky modifikována difenylfosfinovou kyselinou. Výchozí PCN-222 a modifikované MOFy byly charakterizovány práškovou rentgenovou difrakcí a měřením adsorpčních izoterm. Přítomnost navázané difenylfosfinové kyseliny u modifikovaných MOFů byla zdokumentována pomocí elementární analýzy, infračervené spektroskopie, 13 C cross-polarizační NMR a 31 P NMR s rotací pod magickým úhlem. U modifikovaných MOFů byla prokázána vyšší stabilita při vysušení z vody a až čtyřikrát větší produkce singletového kyslíku po ozáření, než u výchozího PCN-222. Klíčová slova: organokovová síť, porfyrin, postsyntetické modifikace, difenylfosfinová kyselina, singletový kyslík, stabilita