Phase transformations in Mg-Zn-based alloys
dc.contributor.advisorStulíková, Ivana
dc.creatorFischer, Josef
dc.date.accessioned2021-03-25T09:03:22Z
dc.date.available2021-03-25T09:03:22Z
dc.date.issued2013
dc.identifier.urihttp://hdl.handle.net/20.500.11956/51681
dc.description.abstractIn this thesis MgZnAlCa and MgZnAl materials were studied. For the study of phase transitions on studied materials the method of measuring the changes of resistivity and hardness was used. The measures were carried out at the temperature of 77 K and at the room temperature. Chosen annealing regimes were 20 K / 20 min and also regime without temperature change - 300 řC. Courses of annealing curves are similar. Material MgZnAlCa shows simpler course of annealing curves than material MgZnAl. With both materials the icosahedral quasicrystalis phase was observed. V této práci byly zkoumány materiály MgZnAlCa a MgZnAl. Pro studium fázových změn ve studovaných materiálech byla použita metoda měření změn rezistivity a tvrdosti. Měření probíhala při teplotě 77 K a při pokojové teplotě. Zvolené žíhací režimy byly 20 K / 20 min a dále režim bez změny teploty - 300 řC. Průběhy žíhacích křivek jsou podobné. Materiál MgZnAlCa vykazuje jednodušší průběh žíhacích křivek než materiál MgZnAl. V obou materiálech byla pozorována icosahedrální kvazikrystalická fáze.en_US
dc.description.abstractIn this thesis MgZnAlCa and MgZnAl materials were studied. For the study of phase transitions on studied materials the method of measuring the changes of resistivity and hardness was used. The measures were carried out at the temperature of 77 K and at the room temperature. Chosen annealing regimes were 20 K / 20 min and also regime without temperature change - 300 řC. Courses of annealing curves are similar. Material MgZnAlCa shows simpler course of annealing curves than material MgZnAl. With both materials the icosahedral quasicrystalis phase was observed. V této práci byly zkoumány materiály MgZnAlCa a MgZnAl. Pro studium fázových změn ve studovaných materiálech byla použita metoda měření změn rezistivity a tvrdosti. Měření probíhala při teplotě 77 K a při pokojové teplotě. Zvolené žíhací režimy byly 20 K / 20 min a dále režim bez změny teploty - 300 řC. Průběhy žíhacích křivek jsou podobné. Materiál MgZnAlCa vykazuje jednodušší průběh žíhacích křivek než materiál MgZnAl. V obou materiálech byla pozorována icosahedrální kvazikrystalická fáze.cs_CZ
dc.languageČeštinacs_CZ
dc.language.isocs_CZ
dc.publisherUniverzita Karlova, Matematicko-fyzikální fakultacs_CZ
dc.titleFázové transformace ve slitinách na bázi Mg-Zncs_CZ
dc.typediplomová prácecs_CZ
dcterms.created2013
dcterms.dateAccepted2013-09-19
dc.description.departmentLaboratory of General Physics Educationen_US
dc.description.departmentKabinet výuky obecné fyzikycs_CZ
dc.description.facultyFaculty of Mathematics and Physicsen_US
dc.description.facultyMatematicko-fyzikální fakultacs_CZ
dc.identifier.repId68571
dc.title.translatedPhase transformations in Mg-Zn-based alloysen_US
dc.contributor.refereeKekule, Tomáš
dc.identifier.aleph001626564
thesis.degree.nameMgr.
thesis.degree.levelnavazující magisterskécs_CZ
thesis.degree.disciplineUčitelství fyziky - matematiky pro střední školycs_CZ
thesis.degree.disciplineTraining Teachers of Physics and Mathematics at Higher Secondary Schoolsen_US
thesis.degree.programPhysicsen_US
thesis.degree.programFyzikacs_CZ
uk.thesis.typediplomová prácecs_CZ
uk.taxonomy.organization-csMatematicko-fyzikální fakulta::Kabinet výuky obecné fyzikycs_CZ
uk.taxonomy.organization-enFaculty of Mathematics and Physics::Laboratory of General Physics Educationen_US
uk.faculty-name.csMatematicko-fyzikální fakultacs_CZ
uk.faculty-name.enFaculty of Mathematics and Physicsen_US
uk.faculty-abbr.csMFFcs_CZ
uk.degree-discipline.csUčitelství fyziky - matematiky pro střední školycs_CZ
uk.degree-discipline.enTraining Teachers of Physics and Mathematics at Higher Secondary Schoolsen_US
uk.degree-program.csFyzikacs_CZ
uk.degree-program.enPhysicsen_US
thesis.grade.csDobřecs_CZ
thesis.grade.enGooden_US
uk.abstract.csIn this thesis MgZnAlCa and MgZnAl materials were studied. For the study of phase transitions on studied materials the method of measuring the changes of resistivity and hardness was used. The measures were carried out at the temperature of 77 K and at the room temperature. Chosen annealing regimes were 20 K / 20 min and also regime without temperature change - 300 řC. Courses of annealing curves are similar. Material MgZnAlCa shows simpler course of annealing curves than material MgZnAl. With both materials the icosahedral quasicrystalis phase was observed. V této práci byly zkoumány materiály MgZnAlCa a MgZnAl. Pro studium fázových změn ve studovaných materiálech byla použita metoda měření změn rezistivity a tvrdosti. Měření probíhala při teplotě 77 K a při pokojové teplotě. Zvolené žíhací režimy byly 20 K / 20 min a dále režim bez změny teploty - 300 řC. Průběhy žíhacích křivek jsou podobné. Materiál MgZnAlCa vykazuje jednodušší průběh žíhacích křivek než materiál MgZnAl. V obou materiálech byla pozorována icosahedrální kvazikrystalická fáze.cs_CZ
uk.abstract.enIn this thesis MgZnAlCa and MgZnAl materials were studied. For the study of phase transitions on studied materials the method of measuring the changes of resistivity and hardness was used. The measures were carried out at the temperature of 77 K and at the room temperature. Chosen annealing regimes were 20 K / 20 min and also regime without temperature change - 300 řC. Courses of annealing curves are similar. Material MgZnAlCa shows simpler course of annealing curves than material MgZnAl. With both materials the icosahedral quasicrystalis phase was observed. V této práci byly zkoumány materiály MgZnAlCa a MgZnAl. Pro studium fázových změn ve studovaných materiálech byla použita metoda měření změn rezistivity a tvrdosti. Měření probíhala při teplotě 77 K a při pokojové teplotě. Zvolené žíhací režimy byly 20 K / 20 min a dále režim bez změny teploty - 300 řC. Průběhy žíhacích křivek jsou podobné. Materiál MgZnAlCa vykazuje jednodušší průběh žíhacích křivek než materiál MgZnAl. V obou materiálech byla pozorována icosahedrální kvazikrystalická fáze.en_US
uk.file-availabilityV
uk.grantorUniverzita Karlova, Matematicko-fyzikální fakulta, Kabinet výuky obecné fyzikycs_CZ
thesis.grade.code3
dc.contributor.consultantSmola, Bohumil
dc.contributor.consultantVlach, Martin
uk.publication-placePrahacs_CZ
uk.thesis.defenceStatusO
dc.identifier.lisID990016265640106986


Files in this item

Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record


© 2017 Univerzita Karlova, Ústřední knihovna, Ovocný trh 560/5, 116 36 Praha 1; email: admin-repozitar [at] cuni.cz

Za dodržení všech ustanovení autorského zákona jsou zodpovědné jednotlivé složky Univerzity Karlovy. / Each constituent part of Charles University is responsible for adherence to all provisions of the copyright law.

Upozornění / Notice: Získané informace nemohou být použity k výdělečným účelům nebo vydávány za studijní, vědeckou nebo jinou tvůrčí činnost jiné osoby než autora. / Any retrieved information shall not be used for any commercial purposes or claimed as results of studying, scientific or any other creative activities of any person other than the author.

DSpace software copyright © 2002-2015  DuraSpace
Theme by 
@mire NV