Termofyzikálne a elektrické vlastnosti keramík na báze illitu
dc.contributor.advisorDobroň, Patrik
dc.creatorCsáki, Štefan
dc.date.accessioned2021-01-11T23:11:43Z
dc.date.available2021-01-11T23:11:43Z
dc.date.issued2018
dc.identifier.urihttp://hdl.handle.net/20.500.11956/104774
dc.description.abstractCSÁKI, Štefan: Thermophysical and electrical properties of illite-based ceramics. [Doctoral thesis]. Constantine the Philosopher University in Nitra. Faculty of Natural Sciences. Charles University. Faculty of Mathematics and Physics. Supervisor: prof. RNDr. Libor Vozár, CSc. (Constantine the Philosopher University in Nitra), doc. Ing. Patrik Dobroň, PhD. (Charles University). Nitra & Prague, 2018. 107 p. Illitic clays are of special importance in the ceramic industry. Therefore, a deep knowledge of the thermophysical processes, as well as the electric properties, is of special importance. The illitic clay originated in Northeastern Hungary was used in this thesis. The reactions, occurring during firing, were studied using thermal analyses (Differential thermal analysis, Thermogravimetry, Thermodilatometry) and special attention was paid to the measurement of the electrical conductivity (both DC and AC). Up to 250 řC, where the removal of the physically bond water (PBW) takes place, the dominant charge carriers were the H+ and OH- ions. After the PBW was removed, Na+ and K+ ions became the dominant charge carriers. During dehydroxylation (450 - 750 řC) H+ and OH- ions were freed from the illite structure, which supported the electrical conduction in the samples. At ~ 970 řC glassy phase appeared...en_US
dc.description.abstractCSÁKI, Štefan: Termofyzikálne a elektrické vlastnosti keramík na báze illitu [Dizertačná práca]. Univerzita Konšntantína Filozofa v Nitre, Fakulta Prírodných vied. Univerzita Karlova. Matematicko-fyzikální fakulta. Školiteľ: prof. RNDr. Libor Vozár, CSc. (Univerzita Konštantína Filozofa v Nitre), doc. Ing. Patrik Dobroň, PhD. (Univerzita Karlova). Nitra a Praha, 2018. 107 s. Illitické hliny sú dôležitou surovinou v keramickom priemysle, a preto sú nevyhnutné podrobné znalosti o procesoch prebiehajúcich počas ich výpalu. V predloženej dizertačnej práci boli skúmané keramiky pripravené z illitickej hliny zo severovýchodného Maďarska. Hlavná pozornosť bola venovaná tepelne aktivovaným procesom a reakciám prebiehajúcim počas ich výpalu a taktiež teplotnej závislosti jednosmernej i striedavej vodivosti. Do teploty 250 řC prebiehalo vyparovanie fyzikálne viazanej vody a dominantnými nosičmi náboja boli H+ a OH- ióny. V teplotnom intervale od 250 řC do 450 řC sprostredkovali elektrickú vodivosť K+ a Na+ ióny. Illit, hlavná zložka illitickej hliny, dehydroxyloval v teplotnom intervale od 450 řC do 750 řC, čo malo za následok uvoľnenie OH- skupín z jeho štruktúry a dominantnými nosičmi náboja sa stali H+ a OH- ióny. Pri teplote ~970 řC sa začala tvoriť sklená fáza, ktorá podporila elektrickú vodivosť v...cs_CZ
dc.languageEnglishcs_CZ
dc.language.isoen_US
dc.publisherUniverzita Karlova, Matematicko-fyzikální fakultacs_CZ
dc.subjectkaolinitcs_CZ
dc.subjectillitcs_CZ
dc.subjectkeramikacs_CZ
dc.subjectakustická emisiacs_CZ
dc.subjecttermofyzikálne a eletrické vlastnostics_CZ
dc.subjectkaoliniteen_US
dc.subjectilliteen_US
dc.subjectceramicen_US
dc.subjectacoustic emissionen_US
dc.subjectthermophysical and electrical propertiesen_US
dc.titleThermophysical and electrical properties of illite-based ceramicsen_US
dc.typerigorózní prácecs_CZ
dcterms.created2018
dcterms.dateAccepted2018-12-18
dc.description.departmentKatedra fyziky kondenzovaných látekcs_CZ
dc.description.departmentDepartment of Condensed Matter Physicsen_US
dc.description.facultyFaculty of Mathematics and Physicsen_US
dc.description.facultyMatematicko-fyzikální fakultacs_CZ
dc.identifier.repId210116
dc.title.translatedTermofyzikálne a elektrické vlastnosti keramík na báze illitucs_CZ
dc.identifier.aleph002222024
thesis.degree.nameRNDr.
thesis.degree.levelrigorózní řízenícs_CZ
thesis.degree.disciplinePhysics of Condensed Matter and Materialsen_US
thesis.degree.disciplineFyzika kondenzovaných soustav a materiálůcs_CZ
thesis.degree.programFyzikacs_CZ
thesis.degree.programPhysicsen_US
uk.thesis.typerigorózní prácecs_CZ
uk.taxonomy.organization-csMatematicko-fyzikální fakulta::Katedra fyziky kondenzovaných látekcs_CZ
uk.taxonomy.organization-enFaculty of Mathematics and Physics::Department of Condensed Matter Physicsen_US
uk.faculty-name.csMatematicko-fyzikální fakultacs_CZ
uk.faculty-name.enFaculty of Mathematics and Physicsen_US
uk.faculty-abbr.csMFFcs_CZ
uk.degree-discipline.csFyzika kondenzovaných soustav a materiálůcs_CZ
uk.degree-discipline.enPhysics of Condensed Matter and Materialsen_US
uk.degree-program.csFyzikacs_CZ
uk.degree-program.enPhysicsen_US
thesis.grade.csProspěl/acs_CZ
thesis.grade.enPassen_US
uk.abstract.csCSÁKI, Štefan: Termofyzikálne a elektrické vlastnosti keramík na báze illitu [Dizertačná práca]. Univerzita Konšntantína Filozofa v Nitre, Fakulta Prírodných vied. Univerzita Karlova. Matematicko-fyzikální fakulta. Školiteľ: prof. RNDr. Libor Vozár, CSc. (Univerzita Konštantína Filozofa v Nitre), doc. Ing. Patrik Dobroň, PhD. (Univerzita Karlova). Nitra a Praha, 2018. 107 s. Illitické hliny sú dôležitou surovinou v keramickom priemysle, a preto sú nevyhnutné podrobné znalosti o procesoch prebiehajúcich počas ich výpalu. V predloženej dizertačnej práci boli skúmané keramiky pripravené z illitickej hliny zo severovýchodného Maďarska. Hlavná pozornosť bola venovaná tepelne aktivovaným procesom a reakciám prebiehajúcim počas ich výpalu a taktiež teplotnej závislosti jednosmernej i striedavej vodivosti. Do teploty 250 řC prebiehalo vyparovanie fyzikálne viazanej vody a dominantnými nosičmi náboja boli H+ a OH- ióny. V teplotnom intervale od 250 řC do 450 řC sprostredkovali elektrickú vodivosť K+ a Na+ ióny. Illit, hlavná zložka illitickej hliny, dehydroxyloval v teplotnom intervale od 450 řC do 750 řC, čo malo za následok uvoľnenie OH- skupín z jeho štruktúry a dominantnými nosičmi náboja sa stali H+ a OH- ióny. Pri teplote ~970 řC sa začala tvoriť sklená fáza, ktorá podporila elektrickú vodivosť v...cs_CZ
uk.abstract.enCSÁKI, Štefan: Thermophysical and electrical properties of illite-based ceramics. [Doctoral thesis]. Constantine the Philosopher University in Nitra. Faculty of Natural Sciences. Charles University. Faculty of Mathematics and Physics. Supervisor: prof. RNDr. Libor Vozár, CSc. (Constantine the Philosopher University in Nitra), doc. Ing. Patrik Dobroň, PhD. (Charles University). Nitra & Prague, 2018. 107 p. Illitic clays are of special importance in the ceramic industry. Therefore, a deep knowledge of the thermophysical processes, as well as the electric properties, is of special importance. The illitic clay originated in Northeastern Hungary was used in this thesis. The reactions, occurring during firing, were studied using thermal analyses (Differential thermal analysis, Thermogravimetry, Thermodilatometry) and special attention was paid to the measurement of the electrical conductivity (both DC and AC). Up to 250 řC, where the removal of the physically bond water (PBW) takes place, the dominant charge carriers were the H+ and OH- ions. After the PBW was removed, Na+ and K+ ions became the dominant charge carriers. During dehydroxylation (450 - 750 řC) H+ and OH- ions were freed from the illite structure, which supported the electrical conduction in the samples. At ~ 970 řC glassy phase appeared...en_US
uk.file-availabilityV
uk.grantorUniverzita Karlova, Matematicko-fyzikální fakulta, Katedra fyziky kondenzovaných látekcs_CZ
thesis.grade.codeP
uk.publication-placePrahacs_CZ
uk.thesis.defenceStatusU


Files in this item

Thumbnail
Thumbnail
Thumbnail
Thumbnail

This item appears in the following Collection(s)

Show simple item record


© 2017 Univerzita Karlova, Ústřední knihovna, Ovocný trh 560/5, 116 36 Praha 1; email: admin-repozitar [at] cuni.cz

Za dodržení všech ustanovení autorského zákona jsou zodpovědné jednotlivé složky Univerzity Karlovy. / Each constituent part of Charles University is responsible for adherence to all provisions of the copyright law.

Upozornění / Notice: Získané informace nemohou být použity k výdělečným účelům nebo vydávány za studijní, vědeckou nebo jinou tvůrčí činnost jiné osoby než autora. / Any retrieved information shall not be used for any commercial purposes or claimed as results of studying, scientific or any other creative activities of any person other than the author.

DSpace software copyright © 2002-2015  DuraSpace
Theme by 
@mire NV